CORRELATING MICROSTRUCTURAL DEVELOPMENT AND FAILURE MECHANISMS TO PHOTOSTIMULATED LUMINESCENCE SPECTROSCOPY AND ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY IN THERMAL BARRIER COATINGS
Title
CORRELATING MICROSTRUCTURAL DEVELOPMENT AND FAILURE MECHANISMS TO PHOTOSTIMULATED LUMINESCENCE SPECTROSCOPY AND ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY IN THERMAL BARRIER COATINGS.
Creator
Jayaraj, Balaji, Sohn, Yongho, University of Central Florida
Abstract / Description
Thermal barrier coatings (TBCs) are widely used for thermal protection of hot section components in turbines for propulsion and power generation. Applications of TBCs based on a clearer understanding of failure mechanisms can help increase the performance and life-cycle cost of advanced gas turbine engines. Development and refinement of robust non-destructive evaluation techniques can also enhance the reliability, availability and maintainability of hot section components in gas turbines...
Show moreThermal barrier coatings (TBCs) are widely used for thermal protection of hot section components in turbines for propulsion and power generation. Applications of TBCs based on a clearer understanding of failure mechanisms can help increase the performance and life-cycle cost of advanced gas turbine engines. Development and refinement of robust non-destructive evaluation techniques can also enhance the reliability, availability and maintainability of hot section components in gas turbines engines. In this work, degradation of TBCs was non-destructively examined by photostimulated luminescence spectroscopy (PSLS) and electrochemical impedance spectroscopy (EIS) as a function of furnace thermal cycling carried out in air with 10-minute heat-up, 0.67, 9.6 and 49.6 -hour dwell duration at 1121°C (2050°F), and 10-minute forced-air quench. TBCs examined in this study consisted of either electron beam physical vapor deposited and air plasma sprayed yttria-stabilized zirconia (YSZ) on a variety of bond coat / superalloy substrates including bond coats of NiCoCrAlY and (Ni,Pt)Al, and superalloys of CMSX-4, Rene'N5, Haynes 230 and MAR-M-509. Detailed microstructural characterization by scanning electron microscopy and energy dispersive spectroscopy was carried out to document the degradation and failure characteristics of TBC failure, and correlate results of PSLS and EIS. Mechanisms of microstructural damage initiation and progression varied as a function of TBC architecture and thermal cycling dwell time, and included undulation of the interface between the thermally grown oxide (TGO) and bond coats, internal oxidation of the bond coats, and formation of Ni/Co-rich TGO. These microstructural observations were correlated to the evolution in compressive residual stress in the TGO scale determined by PSLS shift. Correlations include stress-relief and corresponding luminescence shift towards stress-free luminescence associated with subcritical cracking of the TGO scale and stress-relaxation associated with gradual shift in the luminescence towards stress-free luminescence is related to the undulation of TGO/bondcoat interface (e.g., rumpling and ratcheting). Microstructural changes in TBCs such as YSZ sintering, TGO growth, and subcritical damages within the YSZ and TGO scale were also correlated to the changes in electrochemical resistance and capacitance of the YSZ and TGO, respectively. With thermal exposure the YSZ/TGO resistance and capacitance increased and decreased as result of sintering and TGO growth. With progressive thermal cycling damages in the TGO was related to the TGO capacitance showing a continuous increase and at failure TGO capacitance abruptly increased with the exposure of bondcoat. Further correlations among the microstructural development, PSLS and EIS are documented and discussed, particularly as a function of dwell time used during furnace thermal cycling test, with due respect for changes in failure characteristics and mechanisms for various types of TBCs.
Show less
Date Issued
2011
Identifier
CFE0003635, ucf:48882
Format
Document (PDF)
PURL
http://purl.flvc.org/ucf/fd/CFE0003635
Characterization of Anisotropic Mechanical Performance of As-Built Additively Manufactured Metals
Title
Characterization of Anisotropic Mechanical Performance of As-Built Additively Manufactured Metals.
Creator
Siddiqui, Sanna, Gordon, Ali, Raghavan, Seetha, Bai, Yuanli, Sohn, Yongho, University of Central Florida
Abstract / Description
Additive manufacturing (AM) technologies use a 3D Computer Aided Design (CAD) model to develop a component through a deposition and fusion layer process, allowing for rapid design and geometric flexibility of metal components, for use in the aerospace, energy and biomedical industries. Challenges exist with additive manufacturing that limits its replacement of conventional manufacturing techniques, most especially a comprehensive understanding of the anisotropic behavior of these materials...
Show moreAdditive manufacturing (AM) technologies use a 3D Computer Aided Design (CAD) model to develop a component through a deposition and fusion layer process, allowing for rapid design and geometric flexibility of metal components, for use in the aerospace, energy and biomedical industries. Challenges exist with additive manufacturing that limits its replacement of conventional manufacturing techniques, most especially a comprehensive understanding of the anisotropic behavior of these materials and how it is reflected in observed tensile, torsional and fatigue mechanical responses. As such, there is a need to understand how the build orientation of as-built additively manufactured metals, affects mechanical performance (e.g. monotonic and cyclic behavior, cyclically hardening/softening behavior, plasticity effects on fatigue life etc.); and to use constitutive modeling to both support experimental findings, and provide approximations of expected behavior (e.g. failure surfaces, monotonic and cyclic response, correlations between tensile and fatigue properties), for orientations and experiments not tested, due to the expensive cost associated with AM. A comprehensive framework has been developed to characterize the anisotropic behavior of as-built additively manufactured metals (i.e. Stainless Steel GP1 (SS GP1), similar in chemical composition to Stainless Steel 17-4PH), through a series of mechanical testing, microscopic evaluation and constitutive modeling, which were used to identify a reduced specimen size for characterizing these materials. An analysis of the torsional response of additively manufactured Inconel 718 has been performed to assess the impact of build orientation and as-built conditions on the shearing behavior of this material. Experimental results from DMLS SS GP1 and AM Inconel 718 from literature were used to constitutively model the material responses of these additively manufactured metals. Overall, this framework has been designed to serve as standard, from which build orientation selection can be used to meet specific desired industry requirements.
Show less