- PLASMA PROCESSING FOR RETENTION OF NANOSTRUCTURES.
- Creator
-
Venkatachalapathy, Viswanathan, Seal, Sudipta, University of Central Florida
- Abstract / Description
-
Plasma spray processing is a technique that is used extensively in thermal barrier coatings on gas and steam turbine components, biomedical implants and automotive components. Many processing parameters are involved to achieve a coating with certain functionality. The coating could be required to function as thermal barrier, wear resistant, corrosion resistant or a high temperature oxidation resistant coating. Various parameters, such as, nozzle and electrode design, powder feeding system,...
Show morePlasma spray processing is a technique that is used extensively in thermal barrier coatings on gas and steam turbine components, biomedical implants and automotive components. Many processing parameters are involved to achieve a coating with certain functionality. The coating could be required to function as thermal barrier, wear resistant, corrosion resistant or a high temperature oxidation resistant coating. Various parameters, such as, nozzle and electrode design, powder feeding system, spray distances, substrate temperature and roughness, plasma gas flow rates and others can greatly alter the coating quality and resulting performance. Feedstock (powder or solution precursor) composition and morphology are some of the important variables, which can affect the high end coating applications. The amount of heat a plasma plume has to offer to the particles being processed as a coating depends primarily on the dissociation of the atoms of gaseous mixtures being used to create the plasma and the residence time required for the particle to stay in the flame. The parameters that are conducive for nanostructured retention could be found out if the residence time of the particles in the flame and the available heat in the plume for various gas combinations could be predicted. If the feedstock is a liquid precursor instead of a powder feedstock, the heat that has to be offered by the plasma could be increased by suitable gas combination to achieve a good quality coating. Very little information is available with regard to the selection of process parameters and processing of nano materials feedstock to develop nanostructured coatings using plasma spray. In this study, it has been demonstrated that nano ceramics or ceramic composites either in the form of coatings or bulk free form near net components could be processed using DC plasma spray. For powder feedstock, analytical heat transfer calculations could predict the particle states for a given set of parameters by way of heat input from the plasma to the particles. The parameter selection is rendered easier by means of such calculations. Alumina nano ceramic particles are processed as a coating. During Spray drying, a process of consolidation of nano alumina particles to spherical agglomerates, parameter optimization for complete removal of moisture has been achieved. The parameters are tested for alumina nanoparticles with a plasma torch for the veracity of calculations. The amount of heat transfer from the surface of the agglomerates to the core has been quantified as a function of velocity of particles. Since preparation of nanostructured feedstock for plasma spray is expensive and cumbersome, alternative solution precursor route for direct pyrolysis of precursor to coating has been studied in case of nanocrystalline rare earth oxides. Thus, it has also been shown by this research that nanostructured coatings could be either from a powder feedstock or a solution precursor feedstock. MoSi2-Si3N4, Ni-Al2O3, W-HfC nano ceramic composite systems have been processed as a bulk free form nanocomposite with 60-70% retained nanostructures. The importance of selection of substrates, roughness and the substrate temperature for development of free form bulk components has been highlighted. The improvement in mechanical and high temperature properties associated with having such nanostructured coatings or bulk nanocomposites are revealed. These nanostructured coatings are known for their low thermal conductivity, high wear resistance and can be potentially used as steam and gas turbines coatings for improved thermal efficiency. In summary, bulk nanocomposite through plasma spray processing is a viable alternative to conventional processes such as sintering, HIP for high fracture toughness and hardness applications.
Show less - Date Issued
- 2007
- Identifier
- CFE0001680, ucf:47203
- Format
- Document (PDF)
- PURL
- http://purl.flvc.org/ucf/fd/CFE0001680
- Title
- CHARACTERIZATION AND AQUEOUS COLLOIDAL PROCESSING OF TUNGSTEN NANO-POWDERS.
- Creator
-
Yang, Zhengtao, Sohn, Yongho, University of Central Florida
- Abstract / Description
-
Extensive attention has been paid to consolidate nanoparticles into nanocrystalline components that possess better properties than their coarse-grained counterparts. Nanocrystalline monolithic tungsten (W) has been envisaged to possess better properties than coarse-grained tungsten and to improve the performance of many military components. Commercially available nano-W powders were characterized via X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy...
Show moreExtensive attention has been paid to consolidate nanoparticles into nanocrystalline components that possess better properties than their coarse-grained counterparts. Nanocrystalline monolithic tungsten (W) has been envisaged to possess better properties than coarse-grained tungsten and to improve the performance of many military components. Commercially available nano-W powders were characterized via X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES) and Brunauer, Emmett, and Teller (BET) measurement. While the bulk of nano-W powders consisted of bcc-W as confirmed by XRD and TEM, much of their surface consisted of WO3 with traces of WO2 and WC. Despite the irregular morphology and agglomerates greater than 1 m in size, the diameter of individual nano-W powders ranged from 30 to 100 nm with a surface area of 10.4 m2/g. To obtain green bodies of higher densities and more homogeneous microstructures after consolidation, W nanopowders were de-agglomerated in water and slip cast in plaster molds. De-agglomeration in water was conducted by repeated ultrasonication, washing, centrifuge and pH adjustment. The change in particle size and morphology was examined via SEM. After the initial surface oxide was removed by repeated washing, the reactivity of W nanoparticles to water was somewhat inhibited. Increasing the number of cycles for ultrasonication and washing increased the pH, the degree of de-agglomeration and the stability of W suspension. The zeta potential was more negative with increasing pH and most negative at pH values close to 5. Viscosity also decreased with increasing pH and reached a minimum at a pH 5. To obtain the highest solid loading with the lowest viscosity, the pH value of W suspension was adjusted to 5 using aqueous tetramethylammonium hydroxide solutions. The relative density of the slip cast increased with longer ultrasonic time, increasing slurry pH up to 5, and consequent increase in solids loading. Smaller particles were separated from larger ones by ultrasonication, washing with water and centrifugation. At a 27.8 vol.% solids loading, the size-separated fine W slurry was slip cast into pellets with relative green densities up to 41.3 % and approximate particle sizes of 100 nm. W powders were also ultrasonicated in aqueous poly (ethyleneimine) (PEI) solutions with various concentrations. SEM examinations of particle sizes showed that 1 wt.% PEI led to the optimum dispersion and ultrasonication for longer time with a low power resulted in better dispersion. 0.5 g of W powders were ultrasonicated in 10 ml aqueous poly (allylamine hydrochloride) (PAH) solutions with molar concentrations ranging from 0.01 to 0.05 M. W suspensions with 0.03 M and 0.04 M PAH after two washing cycles showed improved dispersion. Cold isostatic pressing can further increase the green density following slip casting. Sintered slip casts made from de-agglomerated nanoparticle W showed a lower density, more uniform microstructure, smaller grains and smaller pores than the sintered dry pressed pellets.
Show less - Date Issued
- 2009
- Identifier
- CFE0002706, ucf:48144
- Format
- Document (PDF)
- PURL
- http://purl.flvc.org/ucf/fd/CFE0002706